日本日亚BK-47F锻造模具焊条

特 性

熔敷金属含 Cr Mo W V 多元合金，具有优异的耐蚀 耐磨耗 耐冲击性能，焊金可机械加工，淬火硬化优良 硬度HRC 56～58 Deposited metal containing Cr Mo w. v. multielement alloy, excellent corrosion resistance, abrasion resistance to impact resistance welding gold machining, quench hardened high hardness HRC 56-58

用 途

焊补冷作钢\ 冲模 切模 修边模 剪刀 也可以在碳钢和低合金母材上堆焊制成工具Weld-repair cold stamping mould steel \ cutting edge modulus carbon and can also be scissors low alloy parent surfacing made tools

规 格

1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠

特 性

焊金耐热 耐腐蚀 耐磨耗性能优良,用于修复基体合金相似的高温加工工具,如H13钢.

硬度HRC 43～46度A hot work tool steel that is tungsten free,Good hot hardness up to 565℃.For repair of H-13 tool steels and appications in the die casting and forging industries subject to high thermal gradients.

用 途

焊补有色金属压铸模具 PA POM PS PE EP Weld-repair non-ferrous metal die-casting molds PA POM PS PE EP

规 格

1.0￠ 1.2￠ 1.6￠ 2.0￠ 2.4￠

特 性

Cr W V 多元合金焊丝 ，熔敷金属具有自硬性的马氏体组织。具有高硬度耐高温冲击，焊后机加工困难。硬度HRC48～52 Cr multielement alloy welding wire, w. v. deposited metal has since the rigid martensite organization. With high hardness, impact resistant machining difficulty after welding. Hardness HRC48 ~52

用 途

焊补热锻模 冲模 热加工工具 热切模等Hot forging die weld-repair hot-working tools etc. Eagerly

规 格

1.0￠ 1.2￠ 1.6￠ 2.0￠

特 性

焊金耐疲劳 耐热 耐磨耗冲击,一般热压铸模具常有龟裂纹状,大部分是热应力引起,热处理调至适当硬度改善其寿命,硬度太高或太低均不适用.HRC43～47 Welding gold fatigue resistance, abrasion resistance impact resistant heat die-casting molds, most often turtle crack is caused by thermal stress, heat treatment to improve its service life, suitable hardness hardness too much or too little are not applicable.

用 途

焊补热气冲模,铜铝锌热锻模,铝挤压模. Hot stamping, weld-repair copper aluminum and zinc hot forging, aluminum extrusion die

.

规 格

1.0￠ 1.2￠ 1.6￠ 2.0￠

特 性

放电加工,焊接性好,研磨后光滑如镜,加入易切削元素,切削加工容易,溶敷金属具有高韧性,耐磨不变形等特点,焊后只要简单热处理即可得到均一的镜面效果. 750an electro-discharge machining, welding, grinding smooth as a mirror, after joining cutting elements, machining, easy dissolve deposited metal with high toughness and wear no deformation characteristics, such as simple after welding heat can get the mirror effect uniform.

用 途

焊补塑胶模具NAK55 NAK80等NAK55 NAK80 weld-repair plastic mould etc

规 格

1.0￠ 1.2￠ 1.6￠ 2.0￠

特 性

马氏体时效钢,其堆焊层硬度可达HRC30～32度,溶敷金属柔软,具韧性易切削,在其500℃/2H时效处理后硬度可提高到HRC48～50度. Limitation of martensite steel, the hardfacing layer of hardness HRC30 ~ 32 degrees, soluble metal soft, apply, in its toughness cutting 500 ° c / 2H aging treatment can improve HRC48 hardness to 50 ~.

用 途

焊补铝压铸模具,挤压模具,冲裁模 注塑模等. Weld repairs, aluminum casting die, extrusion dies, punching mould injection mold, etc

规 格

1.0￠ 1.2￠ 1.6￠ 2.0￠

特 性

含有W Mo Cr V 的高合金焊丝,溶敷金属具有高韧性,高硬度冲击耐磨耗性能,可使用在600℃的热间环境,焊后金属可高达HRC61～63度,经热处理后硬度尚有提高. Contains W Mo Cr V high alloy welding wire, soluble deposited metal with high toughness and high hardness, impact abrasion resistance performance can be used in 600 degrees Celsius between thermal environment, after welding metal can be as high as HRC61 ~ 63 degree of hardness, still improve.

用 途

焊补冷热作模具,成型刀具,修整刀具 冲头 模具 粉碎机刃口,冲压模具,也可以在碳钢和低合金钢上堆焊制成新工具. Heat for mould weld-repair, molding tool, die cutter punch grinder blade, stamping, also can be in the carbon steel and the low alloy steel made _disibledevent='636'>

0.9￠ 1.2￠ 1.6￠ 2.0￠

牌号

焊条对应型号

堆焊层硬度

HRC

特点及主要用途

HB-YD172(Q)

D172

≥40

用于堆焊齿轮、挖泥斗、矿山机械等磨损件。

HB-YD207(Q)

D207

≥50

用于堆焊推土机刀片，螺旋桨等磨损零件。

HB-YD212(Q)

D212

≥50

常温高硬度堆焊，用于堆焊挖斗、矿山机械等受磨损的机件表面。

HB-YD256(Q)

D256

HB≥170

高锰钢堆焊，适用于破碎机等受冲击磨损部位的堆焊。

HB-YD322(Q)

D322

≥55

用于堆焊各种冲模及切削刃具，兼用于修复要求耐磨损性能较高之机械零件。

HB-YD327A(Q)

≥55

专门用于模具堆焊，耐磨性能高于D322

HB-YD337(Q)

D337

≥48

用于铸钢或锻钢上堆焊锻模。

HB-YD397(Q)

D397

≥40

用于堆焊铸钢或锻钢做坯体的热锻模或堆焊高强度耐磨件。

HB-YD405A(Q)

52-59

用于热轧辊开坯辊堆焊

HB-YD430A(Q)

20-35

用于打底焊

HB-YD488A(Q)

45-50

用于轧辊堆焊

HB-YD507MoA(Q)

35-45

用于阀门堆焊

HB-YD507MoNb(Q)

33-42

用于阀门堆焊

HB-YD518(Q)

40-50

用于连铸辊堆焊

HB-D467Q)

52-55

用于二铁盾构施工刀具刃口堆焊

HB-YD58(Q)

55-62

用于堆焦机磨靴堆焊

HB-YD67(Q)

58-63

用于耐磨表面的堆焊

HB-YD688(Q)

50-55

高铬合金焊丝，用于耐磨打底堆焊

HB-YD888(Q)

55-63

高铬合金焊丝，用于耐磨表面堆焊

HB-YD888Ni(Q)

55-60

高铬合金焊丝，用于耐磨表面堆焊

HB-YD888MoW(Q)

55-60

高铬合金高温耐磨焊丝，耐磨表面堆焊

HB-YD95(Q)

55-63

高铬合金焊丝，用于耐磨表面堆焊

HB-YD988(Q)

55-63

高铬合金焊丝，用于耐磨表面堆焊

HB-YD114(Q)

50-55

高锰钢焊丝，用于受强烈冲击表面堆焊

HB-YD115(Q)

50-55

高锰高铬焊丝，用于受强烈冲击表面堆焊

HB-YD165(Q)

60-65

高硬度耐磨焊丝，适用于磨粒磨损表面堆焊

HB-YD265(Q)

60-65

高硬度耐磨焊丝，适用于磨粒磨损表面堆焊

HB-YD258(Q)

55-60

用于耐磨表面堆焊。